Microstructure evolution of a ti/tib metal-matrix composite during high-temperature deformation

Ozerov, M. S.; Klimova, M. V.; Stepanov, N. D.; Zherebtsov, S. V.

Microstructure evolution of a ti/tib metal-matrix composite during high-temperature deformation

Ozerov, M. S., Klimova, M. V., Stepanov, N. D., Zherebtsov, S. V.

Дата публикации: 2018

Дата публикации в реестре: 2020-07-05T09:21:41Z

Аннотация:

A Ti/TiB metal-matrix composite (MMC) was produced by spark plasma sintering using a Ti-10wt.%TiB2 powder mixture at 850°C under a load of 40 MPa for 15 min. The microstructure evolution and mechanical behavior of the Ti/TiB composite during uniaxial compression at the temperature range 500 - 1050°С was studied

Ключевые слова:
physics, metal-matrix composite, spark plasma sintering, uniaxial compression, dynamic recrystallization, activation energy, precipitation hardening

Тип: Article

Microstructure evolution of a ti/tib metal-matrix composite during high-temperature deformation