Effect of microstructure on the oxidation behavior of a β-solidified γ-TiAl based alloy after nitrogen ion implantation

Panov, D. O.; Sokolovsky, V. S.; Stepanov, N. D.; Zherebtsov, S. V.; Novikov, V. Yu.; Salishchev, G. A.

Effect of microstructure on the oxidation behavior of a β-solidified γ-TiAl based alloy after nitrogen ion implantation

Panov, D. O., Sokolovsky, V. S., Stepanov, N. D., Zherebtsov, S. V., Novikov, V. Yu., Salishchev, G. A.

Дата публикации: 2021

Дата публикации в реестре: 2021-08-05T16:00:33Z

Аннотация:

The microstructure of the oxide layer of a β-solidifying γ-TiAl alloy (Ti-43.2Al-1.9V-1.1Nb-1.0Zr-0.2Gd-0.2B) after nitrogen ion implantation was studied after сyclic oxidation tests at 800 ˚C. Oxidation resulted in the formation of the continuous oxide scale, consisting of thin inner and outer TiO2, dense Al₂O₃ and mixed Al₂O₃ + TiO₂ layers. It was revealed that the nitrogen ion implantation considerably inhibited the growth of the oxide scale, internal oxidation and Al-depleted zones. Thick Al-depleted zones and a mixture of Al2O3 and TiO2 were formed along the colony boundaries

Ключевые слова:
technique, metal science, alloys, oxidation behavior, implantation, nitrogen ion, microstructure, mechanical properties

Тип: Article